Complexes of v or n or nb containing no with organoaluminums as olefin reaction catalysts

ABSTRACT

A CATALYST ACTIVE FOR THE OLEFIN REACTION INCLUDING OLEFIN DISPROPORTIONATION COMPRISING A COMPOUND OF VANADIUM OR NOBIUM COMPLEXED WITH NO AND A SELECTED COMPLEXING AGENT (E.G., BENZOIC ACID) AND COMBINED WITH AN ORGANOALUMINUM COMPOUND (E.G., METHYLALUMINUM SESQUICHLORIDE).

United States Patent 3,562,178 COMPLEXES OF V OR N 0R Nb CONTAINING N0 WITH ORGANOALUMINUMS AS OLEFIN REAC- TION CATALYSTS I William B. Hughes and Ernest A. Zuech, Bartlesville,

Okla., assigno'rs to Phillips Petroleum Company, a corporation of Delaware No Drawing. Continuation-impart of application Ser. No. 635,656, May 3, 1967. This application Jan. 2, 1968, Ser. No. 694,875

Int. Cl. C07c 3/62 US. Cl. 252-429 10 Claims ABSTRACT OF THE DISCLOSURE A catalyst active for the olefin reaction including olefin disproportionation comprising a compound of vanadium or niobium complexed with NO and a selected complexing agent (e.g., benzoic acid) and combined with an organoaluminum compound (e.g., methylaluminum sesquichloride).

This application is a continuation-in-part of copending application Ser. No. 635,656, filed May 3, 1967 now abandoned.

This invention relates to the conversion of olefin hydrocarbons and to a homogeneous catalyst for such conversion. In one aspect, this invention relates to the olefin reaction. In another aspect, it relates to the conversion of olefins to other olefins having difierent molecular weights. In still another aspect, it relates to a homogeneous catalyst.

The term olefin reaction, as used herein, is defined as a process for the catalytic conversion in the presence of a catalyst of a feed comprising one or more ethylenically unsaturated compounds to produce a resulting product which contains at least ten per cent by weight of product compounds, which product compounds can be visualized as resulting from at least one primary reaction, as defined below, or the combination of at least one primary reaction and at least one unsaturated bond isomerization reaction, and wherein the sum of the compounds contained in said resulting product consisting of hydrogen, saturated hydrocarbons, and compounds which can be visualized as formed by skeletal isomerization but which cannot be visualized as formed by one or more of the above-noted reactions, comprises less than twenty-five per cent by weight of the total of said resulting product. Feed components and unsaturated bond isomers thereof are not included in the resulting product for the purpose of determining the abovenoted percentages.

In the olefin reaction, as defined above, the primary reaction is a reaction which can be visualized as comprising the breaking of two existing unsaturated bonds between first and second carbon atoms and between third and fourth carbon atoms, respectively, and the formation of two new unsaturated bonds. Said first and second carbon atoms and said third and fourth carbon atoms can be in the same or different molecules.

The olefin reaction according to this invention is illustrated by the following reactions:

(1) The disproportionation of an acyclic monoor polyene having at least three carbon atoms into other acyclic monoor polyenes of both higher and lower number of carbon atoms; for example, the disproportionation of propylene yields ethylene and butenes; the disproportionation of 1,5-hexadiene yields ethylene and 1,5,9- decatriene;

(2) The conversion of an acyclic monoor polyene having three or more carbon atoms and a difierent acyclic monoor polyene having three or more carbon atoms to 3,562,178 Patented Feb. 9, 1971 ice produce different acyclic olefins; for example, the conversion of propylene and isobutylene yields ethylene and isopentene;

(3) The conversion of ethylene and an internal acyclic monoor polyene having four or more carbon atoms to produce other olefins having a lower number of carbon atoms than that of the acyclic monoor polyene; for example, the conversion of ethylene and 4-methylpentene-2 yields 3-methylbutene-1 and propylene;

(4) The conversion of ethylene or an acyclic monoor polyene having three or more carbon atoms and a cyclic monoor cyclic polyene to produce an acyclic polyene having a higher number of carbon atoms than that of any of the starting materials; for example, the conversion of cyclooctene and 2-pentene yields 2,10-tridecadiene; the conversion of 1,5-cyclooctadiene and ethylene yields 1,5,9- decatriene;

(5) The conversion of one or more cyclic monoor cyclic polyenes to produce a cyclic polyene having a higher number of carbon atoms than any of the starting materials; for example, the conversion of cyclopentene yields 1,6- cyclodecadiene and continued reaction can produce higher molecular weight materials;

(6) The conversion of an acyclic polyene having at least seven carbon atoms and having at least five carbon atoms between any two double bonds to acyclic and cyclic monoand polyenes having a lower number of carbon atoms than that of the feed; for example, the conversion of 1,7- octadiene yields cyclohexene and ethylene; or

(7) The conversion of one or more acyclic polyenes having at least three carbon atoms between any two double bonds to produce acyclic and cyclic monoand polyenes generally having both a higher and lower number of carbon atoms than that of the feed material; for example, the conversion of 1,4-pentadiene yields 1,4-cyclohexadiene and ethylene.

New catalytic processes have been discovered in recent years for the conversion of olefins to other olefin products, including products of both higher and lower molecular weights whereby olefins of relatively low value are converted to olefins of increased value. Such conversions have heretofore been carried out using heterogeneous catalysts comprising compounds such as compounds of molybdenum or tungsten and generally associated with solid materials such as alumina or silica. It has now been found that these olefin conversions can be carried out in a substantially homogeneous state using, as catalysts, selected coordination complexes of niobium or vanadium in combination with aluminum-containing catalytic adjuvants to produce olefins of increased value including solid products, for example, rubber suitable for the manufacture of tires, wire coating, footwear and other industrial products.

It is an object of this invention to provide a method and a catalyst for the conversion of olefin hydrocarbons. It is also an object of this invention to provide a catalyst for the conversion of olefin hydrocarbons. A further object is to provide a homogeneous catalyst for the olefin reaction. Still another object is to provide a method for converting olefins to other olefins of higher and lower number of carbon atoms utilizing a homogeneous catalyst. The provisions of a homogeneous catalyst for converting olefins to other olefins of higher and lower number of carbon atoms is yet another object of the inventoin. Other aspects, objects and advantages of the invention will be apparent to one skilled in the art upon study of the disclosure, including the detailed description of the invention.

Acording to the process of the invention, cyclic olefins, acyclic olefins, and mixtures of these, including mixtures with ethylene, are converted to other olefins by contact with a catalyst system, which forms on admix-ing, under catalyst formation conditions, components comprising (a) Metal complex represented by the formula )a( )h c d]x wherein M is niobium or vanadium; each Z is a halogen, or a CN, SCN, OCN, or SnCl radical; each (L) is selected from R QO, O, CO, [RCO CH], R-SR, 2 )h,

COO/b a is 1-6, b is 1-2, is 1 1, d is 0-6, and the number of Z, (L), and NO groups in the complex is not greater than the number required for the metal to achieve the closed shell electronic configuration of the next higher atomic number inert gas; x is a number indicative of the polymeric state of the complex; R is an aromatic or saturated aliphatic hydrocarbon radical, including radicals which are substituted with groups which do not adversely effect the performance of the finished catalyst such as alkoxy and halo groups, having up to 20 carbon atoms; R is a divalent R radical; R is an aromatic, saturated aliphatic, or ethylenically unsaturated alphatic radical having up to 30 carbon atoms; R is a divalent saturated or ethylenically unsaturated aliphatic radical having from 4 to carbon atoms; R is hydrogen or a methyl radical; and Q is phos phorus, arsenic or antimony; with (b) An aluminum-containing catalytic adjuvant selected from (1) R AlX or (2) a mixture of (1) compounds, or (3) a mixture of one or more R AlX or AlX compounds with one or more compounds represented by R M'X wherein R is an aromatic or saturated aliphatic hydrocarbon radical having up to carbon atoms, including alkoxy and halo derivatives thereof, preferably an alkyl radical having up to 10 carbon atoms; R is hydrogen or R; X is halogen; M is a metal of Group I-A, II-A or III-A; e is an integer from 1 to 3; j" is 0 or an integer from 1 to 2, the sum of e and f being 3; g is an integer from 1 to 3; and h is 0 or an integer from 1 to 2, the sum of g and It being equal to the valence of M. When the adjuvant is (1) and acyclic olefins are converted, f is preferably 1 or 2.

The Group I-A, II-A and III-A metals are those of the Periodic Table of Elements appearing in Handbook of Chemistry and Physics, Chemical Rubber Company, 45th edition (1964).

Some examples of compounds of (1) and (2) are methylaluminum dichloride, dimethylaluminum chloride, methylaluminum sesquichloride, ethylaluminum dichloride, ethylaluminum sesquichloride, di-(Z-ethylhexyl aluminum bromide, phenylaluminum dichloride, di(3-ethoxypropyl) aluminum bromide, benzylaluminum dibromide, dieicosylaluminum bromide, and the like, and mixtures thereof.

Some examples of R' M'X compounds of (3) are phenyllithium, methylsodium, lithium hydride, lithium aluminum hydride, lithium borohydride, diethylzinc, dipropylzine, triethylaluminum, trieicosylaluminum, di(12- chlorododecyl)aluminum chloride, and the like, and mixtures thereof. Prefeerred (b) components of the catalyst system are the (l) or (2) adjuvants.

Metal complex (a) compounds can also be the products formed by the admixture, under complex forming conditions, of a suitable niobium or vanadium compound such as, for example, a halide, oxyhalide, carbonyl, or salt of an organic acid having up to carbon atoms per molecule, or inorganic acid with NO or a nitrosyl halide and with one or more complexing agents selected from and compounds containing the radicals (R NCSS-), R (COO-), (R COR COO'h 0r (CI-IR =CR -CH 4 wherein Q, R, R R R R and b are as previously defined.

Some examples of suitable niobium or vanadium starting compounds are:

NbBI' 5 NbCl NbF NbOBI' NbOCl VBI'3 VCI vc1 VCL; VF

VF 5 VOCl VOBr VOBI'Z VOBI' 3 VO Cl VOCI vocl and the like, and mixtures thereof.

Some examples of suitable complexing agents for the preparation of the metal (a) components of the catalyst system of the present invention are:

triphenylphosphine oxide tribenzylphosphine oxide trimethylarsine oxide tributylstibine oxide tricyclopentylarsine oxide tricyclohexylphosphine oxide trieicosylstibine oxide r tridecylphosphine oxide tri-p-tolylphosphine oxide acetic acid propionic acid butanoic acid Z-methylpropionic acid pentanoic acid hexanoic acid octanoic acid dodecanoic acid hexadecanoic acid octadecanoic acid triacontanoic acid benzoic acid phenylacetic acid oxalic acid malonic acid acetoacetic acid benzoylacetic acid fl-acetylpropionic acid 'y-acetobutyric acid acetonitrile butyronitrile 1,2-cyclohexylenedinitrile ethylenedinitrile acrylonitrile 2,4-pentanedione 1,3-diphenyl-1,3-pentanedione 3,5-heptanedione 4-cyclohexyl-2,4-butanedione ethylsulfide phenylsulfide methylethyl sulfide thiophene tetrahydrothiophene sodium diethyldithiocarbamate potassium dimethyldithiocarbamate Some examples of metal complex (a) components are:

NO-treated benzoic acid-treated NbCl NO-treated (tetrahydrothiophene)NbBr NO-treated (tetrahydrothiophene)NbCl NO-treated (dimethyldithiocarbamate),Nb

NOBr-treated ethylenedinitrile O V acetate 4 NOCl-treated VO (lactate) 2 I NOI-treated (2,4-pentanedionate) V NOCl-treated (2,4-pentanedionate 2 triphenylphosphine oxide)V NOB r-treated (l-phenyl-l ,3-butanedionate) V NO-treated (2,4-pentanedionate) OVC1 NO-treated (acetate) VCl NOCl-treated (1r-ally1) V NOCl-treated (2,4-pentanedionate V NOBr-treated l-phenyl-l,3-butanedionate) V and the like, and mixtures thereof.

The formula [(L),,(NO) M Z is used herein to identify the product obtained by the admixture, under catalyst forming conditions, of the metal compound with one or more ligand-forming materials whether or not the components are present in the complex as indicated in the formula.

When the (a) component of the catalyst system is the product obtained by combining a niobium or vanadium compound with NO or a nitrosyl halide and with one or more ligand-forming materials, the molar proportion of transition metal salt to the selected ligand-former is pref erably in the broad range of from about 0.1:1 to about :1, more preferably about 0.2:1 to 2:1. The products are obtained by combining these ingredients at any convenient temperature, however, excessively high temperatures at which some of the components tend to decompose or excessively low temperatures at which some of the components tend to crystallize or otherwise tend to become unreactive, should be avoided. Generally, it will be preferred to combine the components at a temperature in the range of from about to about 130 C., more preferably 0 to about 60 C., for a time in the range of from a few seconds up to about 24 hours, preferably in the presence of a diluent in which the components of the reaction are at least partially soluble. Any convenient diluent such as carbon tetrachloride, methylene chloride, benzene, cyclohexane, xylene, isooctane, chlorobenzene, and the like, can be used for this purpose. Any order of addition can be used. Such reaction product mixtures need not be isolated but can be used directly in the formation of the catalyst system. In general, the (a) component is fully prepared before contact is made with the (b) component or adjuvant.

The above-described (b) and (a) components of the catalyst system are generally combined, for use in this invention, in proportions in the range of from about 0.1:1 to about 20:1, preferably from about 1:1 to about 10:1 mols of the (b) component to mols of the (a) component. The catalyst is prepared simply by combining these catalyst components under conditions of time and temperature which permit the catalytically active reagent reaciton product to form. This combination occurs very readily and, in general, the components can be mixed at any convenient temperature, avoiding excessively high or low temperatures as stated above, within the range of from about -80 to about 100 C., preferably 0-60 C., for a few seconds or for periods up to several hours in the presence of a diluent in which both the components are at least partially soluble. Any convenient diluent such as benzene, xylene, cyclohexane, chlorobenzene, methylene chloride, ethylene dichloride, and the like, can be used for this purpose. Halogenated diluents are generally preferred. The mixing of these two catalyst components is generally carried out in the substantial absence of air or moisture, generally in an inert atmosphere. After the catalytic mixture is formed, it need not be isolated but can be added directly to the reaction zone as a solution in its preparation solvent. If desired, the catalyst components can be separately added, in any order, to the reaction zone either in the presence or absence of the feed olefin.

Olefins applicable for use in the process of the invention are nontertiary, non-conjugated, acyclic monoand polyenes having at least 3 carbon atoms per molecule including cycloalkyl, cycloalkenyl and aryl derivatives thereof; cyclic monoand polyenes having at least 4 carbon atoms per molecule including alkyl and aryl derivatives thereof; mixtures of the above olefins; and mixtures of ethylene and the above olefins. Many useful reactions are accomplished with such cyclic olefins having 4-30 carbon atoms per molecule. Non-tertiary olefins are those wherein each carbon atom, which is attached to another carbon atom by means of a double bond, is also attached to a hydrogen atom.

Some specific examples of acyclic olefins suitable for reactions of this invention include propylene, l-butene, 2- butene, l-pentene, Z-pentene, l-hexene, 1,4-hexadiene, 2- heptene, 4-methyl-2-Octene, l-octene, 2,5-octadiene, 2-nonene, l-dodecene, 2-tetradecene, l-hexadecene, l-phenylbutene 2,4 octene, 3-eicosene, 3-hexene, 1,4-pentadiene, 1,4,7-dodecatriene, 4-methyl-4-octene, 4-vinylcyclohexene, 1,7-octadine, 1,5-eicosadiene, Z-triacontene, 2,6-dodecadiene, 1,4,7,10,13-octadecapentaene, 8-cyclopentyl-4,5- dimethyl-l-decene, 6,6-dimethyl-1,4-octadiene, and 3- heptene, and the like, and mixtures thereof.

Some specific examples of cyclic olefins suitable for the reaction of this invention are cyclobutene, cyclopentene, cycloheptene, cyclooctene, 5-n-propylcyclooctene, cyclodecene, cyclododecene, 5,5,4,4-tetramethylcyclononene, 3,4,5,6,7-pentaethylcyclodecene, 1,5-cyclooctadiene, 1,5,9- cyclododecatriene, l,4,7,10-cyclododecatetraene, 6-methyl-6-ethyl-cyclooctadiene-1,4, and the like, and mixtures thereof.

It will be understood by those skilled in the art that not all olefinic materials will be converted by the present invention with equal effectiveness. The reactions described in the present invention are equilibrium-limited reactions and, barring the selective removal of one or more products from the reaction zone, the extent of conversion will depend upon the thermodynamics of the specification system observed. Thus, conversion of olefinic materials to give specific products can be thermodynamically favored while the reverse reaction is very slow and ineffective. For example, 1,7-octatriene is converted to equilibriumfavored products such as cyclohexene and ethylene. The reverse reaction of ethylene and cyclohexene, correspondingly, goes very poorly. Other well known factors, such as steric hindrance in bulky molecules, significantly and sometimes drastically affect the rates of reaction of some olefins such that extremely long reaction times are re quired.

The reaction of symmetrical monoolefins with themselves, to give different olefin products, will sometimes proceed very slowly, requiring some double bond migration to take place before the reaction will proceed at a significant rate. For the same reason, the conversion of a mixture of ethylene and a l-olefin for example can be more difficult than the conversion of ethylene with an internal olefin, some double bond isomerization also being required in this instance.

It has also been found that branching also retards the Olefin reactivity in proportion to its propinquity to the reacting double bond. Analogously, the presence of inert polar substituents on the olefinic compound appears tolerable only if located some distance from the double bond.

Thus, the present invention is directed primarily to the to the conversion of those olefins or combinations of olefins which are capable of undergoing the olefin reaction to a significant degree when contacted with the catalyst of the present invention under reaction conditions suitable for effecting the olefin reaction.

Presently preferred olefinic feed compounds are those contained in the following classes:

(1) Acyclic monoolefins, including those with aryl, cycloalkyl, and cycloalkenyl substituents, having 3-20 carbon atoms per molecule with no branching closer than about the 3-position and no quaternary carbon atoms or aromatic substitution closer than the 4-position to the double bond, and mixtures of such unsubstituted acyclic monoolefins. Some examples of these are: propylene, pentene-l, pentene-2, butene-l, butene-Z, 3-methylbutene- 1, hexene-Z, octene-4, nonene-2, 4-methylpentene-l, decene-3, 8-ethyldecene-2, dodecene-4, vinylcyclohexene, 4- vinylcyclohexene, eicosene-l, and the like.

(2) A mixture of ethylene and one or more acyclic unsubstituted internal monoolefins of (1). Some examples of such mixtures are: ethylene and butene-2, ethylene and pentene-2, ethylene and hexene-3, ethylene and heptene-3, ethylene and 4-methylpentene-2, ethylene and octene-4, ethylene and dodecene-4, and the like.

(3) Acyclic, non-conjugated polyenes having from 5 to about 20 carbon atoms per molecule, containing from 2 to about 4 double bonds per molecule and having at least one double bond with no branching nearer than the 3-position and no quaternary carbon atom nearer than the 4-position to that double bond, or mixture of such polyenes. Some examples are: 1,4-pentadiene, 1,5-hexadiene, 1,7-octadiene, 2,6-decadiene, 1,5,9-dodecatriene, 4- methylheptadiene-l,6, 1,7-octadiene, 1,6-octadiene, and the like.

(4) A mixture of ethylene and one or more acyclic polyenes of (3) which contain at least one internal double bond. Some examples are: ethylene and 1,6-octadiene, ethylene and 1,5-decadiene, and the like.

(5) Cyclopentene.

(6) Monocyclic and bicyclic monoolefins having 7 t 12 ring carbon atoms, including those substituted with up to 3 alkyl group shaving up to about carbon atoms, with no brnaching closer than the 3-position and with no quaternary carbon atoms closer than the 4-position to that double bond, and mixtures of such olefins including mixtures with cyclopentene. Some examples are: cycloheptene, cyclooctene, 4-methylcyclooctene, 3-methyl-5-ethylcyclodecene, cyclononene, cyclododecene, norbornene, and the like.

(7) A mixture of one or more of the monocyclic olefins of (6) with either ethylene or with one or more unsubstituted acyclic monoolefins of (1). Some examples of these are: ethylene and cycloheptene, ethylene and cyclooctene, propylene and cyclodecene, pentene-2 and cyclooctene, ethylene and cyclododecene, and the like.

(8) Monocyclic and bicyclic non-conjugated polyenes having from 5 to about 12 ring carbon atoms, including those substituted with up to 3 alkyl groups having up to about 5 carbon atoms each, having at least one double bond with no branching closer than the 3-position and with no quaternary carbon atoms closer than the 4-position to that double bond, and mixtures thereof. Some examples of these are: 1,5-cyclooctadiene, 1,5,9-cyclododecatriene, 1,4-cycloheptadiene, norbornadiene, and the like.

(9) A mixture of one or more monocyclic polyenes of (8) with one or more acylic l-olefins having from 2 to about 10 carbon atoms, having no branching nearer than the 3-position and no quaternary carbon atoms nearer than the 4-position to the double bond. Some examples of these are: 1,5-cyclooctadiene and ethylene, 1,5,9-cyclododecatriene and ethylene, 1,5,9-cyclododccatriene and pentene-l, and the like.

(10) Polar group-substituted olefin compounds of classes 1) through (9) containing from about 5 to about carbon atoms per molecular in which the polar group, such as halogen atom, is sufficiently removed from the active double bond (generally, no nearer to the double bond than the 5-position) so as not to interfere with the reaction, and mixtures with unsubstituted members of class (1). Some examples are: 5chloropentene-l, a mixture of pentene-Z and S-chloropenten-l, and the like.

According to the process of the invention, the conversion of the olefin or mixture of olefins can take place at any conventient temperature in the broad range of 30 to about 150 C., preferably 0 to C. The conversion can be carried out at any convenient pressure which is sufficient to maintain a liquid phase Within the reaction zone. A diluent such as the used in the catalyst preparation or another inert solvent can be used in the reaction if desired. In general, any inert diluent which will maintain a substantially homogeneous reaction phase can be used. The time of contact will depend upon the desired degree of conversion with the specific feed olefins and the speclfific catalysts used but will, generally, be in the range of from about 0.1 minute to about 20 hours, preferably 5 to 120 minutes. The proportion of the catalyst composition to olefin feed in the recation zone will generally be in the range of about 0.001- millimoles of niobium or vanadium per mole of olefin feed.

Any conventional contacting technique can be utilized for the olefin conversion and batchwise or continuous operation can be utilized. After the reaction period, the products can be separated and/or isolated by conventional means such as by fractionation, crystallization, adsorption, and the like. Unconverted feed materials or products not in the desired molecular weight range can be recycled. If desired, the catalyst can be destroyed by treatment with sufficient water or alcohol to deactivate the catalyst prior to the separation of the products. In some cases, the catalyst which is separated from the products can be recycled to the reaction zone for additional use.

The invention can be further illustrated by the following example.

EXAMPLE An 0.81 g. (0.003 mole) quantity of NbCl was mixed with 30 ml. of chlorobenzene and 0.73 g. of benzoic acid in a nitrogen-purged 7-ounce reaction bottle. The contents of the bottle were then treated with gaseous NO at 25 p.s.i.g. for 1 hour at room temperature. The reactor was vented, evaculated, and flushed with nitrogen. A 5 ml. portion of the above mixture was then mixed with 5 ml. cholorobenzene, 0.5 methylalu'minum sesquichloride, and 10 ml. pentene-2 in a dry nitrogen purged 7-ounce reaction bottle and the mixture was allowed to react at room temperature, with stirring, for 30 minutes.

A sample of the reaction mixture was analyzed by gasliquid chromatography, and the olefin content was found to be as follows, in weight percent:

Butenes 1.7 Pentenes 96.3 Hexenes 2.1

Some heavier polymeric material was also obtained.

In the practice of the process of this invention, the feed olefins, catalysts and operating conditions disclosed include combination wherein solid, hubbery materials are produced; for example, if a propylene feed and a suitable aluminum-containing adjuvant such as methylaluminum sesquihalide or methylaluminum dihalide are used a solid, rubbery material is produced having characteristics of ethylene-propylene rubber. This rubbery material is useful in the manufacture of tires, wire coating, footwear and other industrial products.

The homogeneous catalysts of this invention can be deposited upon a suitable support or carrier and used in the olefin reaction, preferably where the olefin feed is in the vapor phase. Catalyst supports in clude solid, inorganic or organic materials conventionally used as catalyst supports or carriers such as silica, alumina, silicaalumin, titania, boria, zeolites, ion exchange resins, solid polymers containing functional groups such as those prepared by the polymerization of 4- vinylpyridine, vinyl dimethylphosphine, and the like.

The support can be impregnated with the homogeneous catalyst by wetting the support with a solution of the solution of the catalyst in a solvent which is then evaporated. Among solvents suitable are relatively low-boiling organic solvents such as pentane, methylene chloride,

cyclohexane, and the like. The amount of homogeneous catalyst added to the support will be from 0.1 to about 30 weight percent of the total of the catalyst and support. If the support is to be activated by calcination, it is usually activated prior to the impregnation step.

Impregnation and evaporation condition in preparing the catalyst are conventional, being carried out at temperature up to about 150 C. Operating conditions in carrying out the olefin reaction are the same for the supported and the nonsupported homogeneous catalyst systems.

That which is claimed is:

1. A catalyst consisting essentially of (a) a metal complex represented by the formula [(L),,(NO),,M Z wherein M is niobium or vanadium; each Z is a halogen, CN, SCN, OCN, or SnCl radical; each (L) is a ligand represented by the formula R QO, O, CO, [(RCO CH-], R-SR, 2 5( )b R (COO n oou ooo or (CHR CR CHa- A \J a is 1-6, b is 12, is 1-4, d is 0-6, and the number of Z, (L), and NO groups in the complex is not greater than the number required for the metal to achieve the closed shell electronic configuration of the next higher atomic number inert gas; x is the number of the polymeric state of the complex; R is an aromatic or saturated aliphatic hydrocarbon radical having up to 20 carbon atoms per molecule including alkoxy and halo derivatives thereof; R is a divalent R radical; R is a divalent saturated or ethylenically unsaturated aliphatic radical having from 4 to 10 carbon atoms; R is hydrogen or a methyl radical; R is an aromatic, saturated aliphatic, or ethylenically unsaturated aliphatic radical having up to 30 carbon atoms; and Q is phosphorus, arsenic or antimony; with (b) an aluminum-containing catalytic adjuvant which is (1) R AlX or (2) a mixture of (1) compounds, or (3) a mixture of one or more R AlX or AlX compounds with one or more compounds represented by R' MX wherein R is as defined above; R is hydrogen or R; X is halogen; M is a metal of Group I-A, II-A or III-A; e is an integer from 1 to 3; f is 0 or an integer from 1 to 2, the sum of e and 1 being 3; g is an integer from 1 to 3; and h is 0 or an integer from 1 to 2, the sum of g and h being equal to the valence of M, and wherein the molar proportions of (b) to (a) is about 0.1:1 to about 20:1. 2. A catalyst consisting essentially of an admixture of (a) a niobium or vanadium halide, oxyhalide, carbonyl, cyanide, thiocyanate, cyanate, trichlorostannate, or a salt of a hydrocarbon carboxylic acid having up to 30 carbon atoms per molecule, with NO or a nitrosyl halide and with one or more complexing agents capable of complexing with said metal represented by the formula: R QO; RCOCH COR;

alkali metal dihydrocarbyldithiocarbamates; acids of the formula R (COOH) or ketoacids of the formula R COR COOH; wherein R is an aromatic or saturated aliphatic hydrocarbon radical having up to 20 carbon atoms including alkoxy and halo derivatives thereof, R is a divalent R radical, R is a divalent saturated or ethylenically unsaturated aliphatic radical having 4 to carbon atoms, R is 10 an aromatic, saturated aliphatic, or ethylenically unsaturated aliphatic radical having up to 30 carbon atoms, Q is phosphorus, arsenic or antimony, and b is an integer from 1 to 2; and

(b) an aluminum-containing adjuvant which is a compound represented by the formula e r (2) a mixture of (1) compounds, or (3) a mixture of one or more R AlX or AlX compounds with one or more compounds represented by R MX wherein R is as defined above; R is hydrogen or R; X is halogen; M is a metal of Group I-A, II-A or IIIA; e is an integer from 1 to 3; f is 0 or an integer from 1 to 2, the sum of e and f being 3; g is an integer from 1 to 3; and h is 0 or an integer from 1 to 2, the sum of g and 11 being equal to the valence of M, and wherein the molar proportion of (b) to (a) is in the range of from about 0.1:1 to about 20:1,

3. The composition of claim 1 wherein the (b) component is (l) or (2).

4. The composition of claim 2 wherein the (b) component is (1) or (2).

5. The composition of claim 1 further including a diluent in which the (a) and (b) components are at least partially soluble.

'6. The composition of claim 2 further including a diluent in which the (a) and (b) components are at least partially soluble.

7. The compositio not claim 5 wherein the diluent is benzene, xylene, cyclohexane, chlorobenzene, methylene chloride or ethylene chloride.

8. The composition of claim 1 further including a solid inorganic or organic support or carrier selected from the group consisting of silica, alumina, silica-alumina, titania, boria, zeolites, ion exchange resins, a solid polymer of 4-vinylpyridine and a solid polymer of vinyl dimethylphosphine.

9. The composition of claim 2 wherein the (a) component of the catalyst system is formed by combining the metal compound with NO or a nitrosyl halide and with one or more of the complexing agents in a molar proportion of the metal compound to the complexing agent in the range of from about 0.1:1 to about 10:1 at a temperature range of about -25 to about C. for a few seconds up to about 24 hours in the presence of a diluent in which the metal compound and ligand-former are at least partially soluble.

10. A composition according to claim 2 wherein the (a) component is NbCl complexed with benzoic acid and NO; and the (b) component is methylaluminum sesquichloride.

References Cited UNITED STATES PATENTS 3,016,371 1/1962 Natta et a1 252429(A)X 3,054,754 9/1962 Lasky 252429 (B) 3,063,979 11/1962 Truett et a1. 252429(A)X 3,281,375 10/ 1966 Vandenberg 252429(A) 3,294,828 12/1966 Werner 252431(N)X 3,379,706 4/1968 Wilke 25243 1X 3,400,113 9/1968 Winter et al. 252-429(B)X 3,427,365 2/ 1969 Maxfield 252-431(P)X 3,444,149 5/1969 Kelly 252429(B)X 3,446,871 5/1969 Maxfield 252431(N)X PATRICK P. GARVIN, Primary Examiner US. Cl. X.R.

UNITED STATES PATENT OFFICE CERTIFICATE OF CORRECTION Patent N 3,562,178 William B. Hughes et a1 Dated: February 9, 15

It is certified that error appears in the above-identified patent and that Letters Patent. are hereby corrected as shown below:

011- should be [(RCO2) column 9, line 19,

Column 9, line 18, "[(RCO CH-l column 9,

65 (CN) should be "8 should be (12 R (61% column 9, line 20, "(cHR -cR -cH 4" should be (CHB -CR -CE Q column 10, line 32, "compositio 1101" should be composition 0? Signed and sealed this 28th day of December 1 971 (SEAL) Attest:

EDWARD M.FLETCHER,JR. ROBERT GOTTSGHALK Acting Commissioner of Paten Attesting Officer 